Packaging Type
15 lt.
Description
Acrylic emulsion based primer to increase the adherence of gypsum and cement based liquids to the surface for exposed concrete surfaces, walls and ceilings
Color Usage Areas
Green It is applied on walls, columns and ceilings before gypsum and cement based plaster applications.
Properties
It is an easy-to-apply primer that increases the adherence of cement and gypsum based plaster mortars to exposed concrete surfaces, prevents rapid water loss of these materials and extends the working time.
Technical Specifications
- Binder Type: Acrylic copolymer
- Viscosity (KU)(25 °C): 135 ± 5 (thinning with 10% water)
- Density (g/ml) (20 °C): 1.52 ± 0.03
- pH: 8.00-9.00
- Application Thickness: Max. 0.4 mm
- Area that can be primed: Depending on the surface, 4-7 m² area can be primed with 1 kg in a single coat.
- Drying Time (20 °C): Drying: 2 hours,
- Thinning Rate : 30-40% (with water)
- Consumption: Approx. 150-250 gr/m² on the surface
- Solids (Wt) (%): 78 ± 2
Application 1
There should be no loose particles on the application surfaces. All oil, grease, rust, dust and paraffin residues must be removed from the surface.
Application 2
Depending on the desired fluidity, it is diluted with 30 - 40% water and mixed with a low speed mixer for about 4 - 5 minutes, after obtaining a homogeneous and lump-free mixture, it is applied as a single coat on the prepared surface with an exterior roller. The product should be mixed at certain intervals during application.
Storage Conditions
It can be stored in its original packaging in 5-35 °C environments away from direct sunlight. Protect from extreme temperature, humidity and frost.
Important Warnings
The primer must be thoroughly mixed before use. Ambient temperature should be between 5-35 °C during application. After each application; brush or roller should be cleaned with water. The primed surfaces should be protected from physical and chemical factors for 24 hours. The primer should never be discharged into sewage and water channels. Application should be done as stated above.